PU Adhesive Sealant For Windshield Repair Supplier XYG Auto Glass China
Technical date
Items | Renz10 | |
Scope | Typical value | |
Appearance | Black, homogeneous paste | / |
Extrudability (ml/min) GB/T 13477.4 | ≥60 | 98 |
Sagging properties(mm) GB/T 13477.6 | 0 | 0 |
Tack free time(min) GB/T 13477.5 | 10~30 | 20 |
Curing speed(mm/d)HG/T 4363 | ≥3.0 | 3.5 |
Non-volatile contents (%)GB/T 2793 | ≥95 | 96 |
Shore A-hardness GB/T 531.1 | 55~65 | 60 |
Tensile strength(MPa) GB/T 528 | ≥4.5 | 5.2 |
Elongation at break(%) GB/T 528 | ≥400 | 450 |
Tear strength( N/mm) GB/T 529 | ≥8.0 | 9.4 |
Tensile-shear strength(MPa) GB/T 7124 | ≥2.5 | 3.0 |
Operating temperature(ºC) | -40~90 | |
Direction for use = 1 * GB3 All data above were tested under standardized condition at 23±2ºC.50±5%RH.